We present a comprehensive study of the synthesis, structure, and magnetic properties of the honeycomb oxide Na3Mn2SbO6 supported by neutron diffraction, heat capacity, and magnetization measurements. The refinements of the neutron diffraction patterns (150, 50, and 45 K) using the Rietveld method confirm the monoclinic (S. G. C2/m) structure. Temperature-dependent magnetic susceptibilities measured at varying fields along with the heat capacity measurements demonstrate the coexistence of long-range ordering (∼42 K) and short-range ordering (∼65 K). The field-dependent isothermal magnetization measurements at 5 K indicate a spin-flop transition around 5 T. Rietveld refinements of the low-temperature (below 45 K) neutron diffraction data further confirm the long-range magnetic ordering. In addition, the temperature variation of the lattice parameters obtained from the neutron powder diffraction analysis exhibited a distinct anomaly near the antiferromagnetic transition temperature. The appearance of the concomitant broadened backgrounds in the neutron powder diffraction data collected at 80, 50, and 45 K supports the short-range ordering. The resultant magnetic structure consists of spins that are aligned antiparallel with the nearest neighbors and also with the spins of the adjacent honeycomb layers. The occurrence of a fully ordered magnetic ground state (Neel antiferromagnetic (AFM)) in Na3Mn2SbO6 consolidates the significance of fabricating new honeycomb oxides.