Flexible photonic devices based on soft polymers enable real-time sensing of environmental conditions in various industrial applications. A myriad of fabrication techniques have been established for producing optical devices, including photo and electron-beam lithography, nano/femtosecond laser writing, and surface imprinting or embossing. However, among these techniques, surface imprinting/embossing is simple, scalable, convenient to implement, can produce nanoscale resolutions, and is cost-effective. Herein, we utilize the surface imprinting method to replicate rigid micro/nanostructures onto a commonly available PDMS substrate, enabling the transfer of rigid nanostructures into flexible forms for sensing at a nanometric scale. The sensing nanopatterned sheets were mechanically extended, and the extension was remotely monitored via optical methods. Monochromatic light (450, 532, and 650 nm) was transmitted through the imprinted sensor under various force/stress levels. The optical response was recorded on an image screen and correlated with the strain created by the applied stress levels. The optical response was obtained in diffraction pattern form from the flexible grating-based sensor and in an optical-diffusion field form from the diffuser-based sensor. The calculated Young's modulus in response to the applied stress, measured through the novel optical method, was found in a reasonable range compared to the reported range of PDMS (360-870 kPa) in the literature.
Keywords: PDMS; diffraction pattern; optical diffusion; photonics devices; surface imprinting.