Results of experimental investigation on the mitigation of alkali-silica reaction (ASR) by low-grade calcined clay are presented. Domestic clay with an Al2O3 content equal to 26% and SiO2-58% was used. The calcination temperatures were as follows: 650 °C, 750 °C, 850 °C and 950 °C, which were chosen much more widely than presented in previous studies. Pozzolanity of the raw and calcined clay was determined with the Fratini test. The performance of calcined clay to mitigate ASR was evaluated according to ASTM C1567 using reactive aggregates. A control mortar mixture was prepared with 100% Portland cement (Na2Oeq = 1.12%) as a binder with reactive aggregate, and test mixtures were made with 10% and 20% of calcined clay as a cement replacement. The microstructure of the specimens was observed on the polished sections using scanning electron microscope (SEM) operated in backscattered mode (BSE). The results of expansion of mortar bars with reactive aggregate showed that replacing cement with calcined clay reduced the expansion of the mortar bars. The greater the cement replacement, the better results in terms of ASR mitigation. However, the influence of the calcination temperature was not as clear. The opposite trend was found with the use of 10% or 20% calcined clay.
Keywords: Fratini test; alkali–silica reaction (ASR); expansion; low grade calcined clay; microscopic analysis; mitigation.