This work presents an experimental study on the physico-mechanical and microstructural characteristics of stabilised soils and the effect of wetting and drying cycles on their durability as road subgrade materials. The durability of expansive road subgrade with a high plasticity index treated with different ratios of ground granulated blast furnace slag (GGBS) and brick dust waste (BDW) was investigated. Treated and cured samples of the expansive subgrade were subjected to wetting-drying cycles, California bearing ratio (CBR) tests, and microstructural analysis. The results show a gradual reduction in the California bearing ratio (CBR), mass, and the resilient modulus of samples for all subgrade types as the number of cycles increases. The treated subgrades containing 23.5% GGBS recorded the highest CBR value of 230% under dry conditions while the lowest CBR value of 15% (wetting cycle) was recorded for the subgrade treated with 11.75% GGBS and 11.75% BDW at the end of the wetting-drying cycles, both of which find useful application in road pavement construction as calcium silicate hydrate (CSH) gel was formed in all stabilised subgrade materials. However, the increase in alumina and silica content upon the inclusion of BDW initiated the formation of more cementitious products due to the increased availability of Si and Al species as indicated by EDX analysis. This study concluded that subgrade materials treated with a combination of GGBS and BDW are durable, sustainable and suitable for use in road construction.
Keywords: California bearing ratio; brick dust waste; durability; expansive subgrade; microstructural; sustainable soil stabilisation; wetting–drying.