The effect of final thermomechanical treatment (FTMT) on the mechanical properties and microstructure of a T-Mg32(Al Zn)49 phase precipitation hardened Al-5.8Mg-4.5Zn-0.5Cu alloy was studied. The as-cold rolled aluminum alloy samples were subjected sequentially to solid solution treatment, pre-deformation, and two-stage aging treatment. Vickers hardness was measured during the aging process under various parameters. Tensile tests were conducted on the representative samples based on the hardness results. Microstructural characteristics were analyzed via transmission electron microscopy and high-resolution transmission electron microscopy. The conventional T6 process was also carried out for comparison. The hardness and tensile strength are increased evidently by the FTMT process for the Al-Mg-Zn-Cu alloy, while the ductility is adversely affected to a small extent. The precipitation at the T6 state consists of a coherent Guinier-Preston zone and T″ phase in the form of intragranular, fine, and spherical particles, while a semi-coherent T' phase appears after the FTMT process as a new constituent. The distribution of dislocation tangles and isolated dislocations is another feature of FTMT samples. Enhanced precipitation hardening and dislocation strengthening account for the improved mechanical performance of FTMT samples.
Keywords: Al-Mg-Zn-Cu alloy; T phase; aging; hardness; tensile property; thermomechanical treatment.