Complex oxide films stabilized by epitaxial growth can exhibit large populations of point defects which have important effects on their properties. The site occupancy of pulsed laser-deposited epitaxial terbium iron garnet (TbIG) films with excess terbium (Tb) is analyzed, in which the terbium:iron (Tb:Fe)ratio is 0.86 compared to the stoichiometric value of 0.6. The magnetic properties of the TbIG are sensitive to site occupancy, exhibiting a higher compensation temperature (by 90 K) and a lower Curie temperature (by 40 K) than the bulk Tb3 Fe5 O12 garnet. Data derived from X-ray core-level spectroscopy, magnetometry, and molecular field coefficient modeling are consistent with occupancy of the dodecahedral sites by Tb3+ , the octahedral sites by Fe3+ , Tb3+ and vacancies, and the tetrahedral sites by Fe3+ and vacancies. Energy dispersive X-ray spectroscopy in a scanning transmission electron microscope provides direct evidence of TbFe antisites. A small fraction of Fe2+ is present, and oxygen vacancies are inferred to be present to maintain charge neutrality. Variation of the site occupancies provides a path to considerable manipulation of the magnetic properties of epitaxial iron garnet films and other complex oxides, which readily accommodate stoichiometries not found in their bulk counterparts.
Keywords: complex oxides; defect engineering; epitaxial stabilization; garnets; magnetic thin films.
© 2023 Wiley-VCH GmbH.