Current research deals with thermoplastic polyamide (PA6)-based composites reinforced with basalt and Kevlar fabrics. Hybrid composites were developed by altering the stacking sequence of basalt and two kinds of Kevlar fabrics. Pure-basalt- and pure-Kevlar-based samples were also developed for comparison purposes. The developed samples were evaluated with respect to mechanical and thermomechanical properties. Mechanical tests, e.g., tensile, flexural, and impact strength, were conducted along with thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) to ascertain the load-bearing and high-temperature stability of the hybrid composite samples vis-à-vis pure-basalt- and Kevlar-based samples. Scanning electron microscopy (SEM) was carried out to study the nature of fracture and failure of the composite samples. The pure-basalt-based PA6 thermoplastic composites exhibited the best mechanical performance. Hybridization with basalt proved to be beneficial for improving the mechanical performance of the composites using Kevlar fabrics. However, a proper stacking sequence and density of Kevlar fabric has to be selected. The thermogravimetric analysis showed minimal weight loss for basalt-based composites. Furthermore, the thermal stability of the composites using Kevlar fabric was improved by hybridization with basalt fabric. The thermomechanical characteristics of hybrid composites may be altered by changing the stacking order of the reinforcements. Differential scanning calorimetry further established that the hybrid composites with alternate layers of basalt and Kevlar can improve the heat flow rate and enable survivability at extreme temperatures. Such novel hybrid composites can be used for high-load-bearing and high-temperature applications, e.g., defense, aerospace, automotives, and energy applications.
Keywords: Kevlar; basalt; differential scanning calorimetry (DSC); hybrid composite; mechanical test; scanning electron microscopy (SEM); thermogravimetric analysis (TGA); thermoplastic.