New ways of recycling fly ash are of great significance for reducing the environmental pollution. In this work, biodegradable hydrophobic poly (L-lactic acid)/fly ash composites for anti-icing application were successfully fabricated via a facile solvent-volatilization-induced phase separation approach. A silane coupling agent of 3-(Trimethoxysilyl) propyl methacrylate was used to decorate a fly ash surface (FA@KH570) for strengthening the interface bonding between fly ash and poly (L-lactic acid). Moreover, FA@KH570 could obviously enhance the crystallinity of poly (L-lactic acid) (PLLA)/FA@KH570 composites, which accelerated the conversion from the liquid-liquid to the liquid-solid phase separation principle. Correspondingly, the controllable surface morphology from smooth to petal-like microspheres was attained simply by adjusting the FA@KH570 content. After coating nontoxic candle grease, the apparent contact angle of 5 wt% PLLA/FA@KH570 composite was significantly increased to an astonishing 151.2°, which endowed the composite with excellent anti-icing property. This strategy paves the way for recycling waste fly ash and manufacturing hydrophobic poly (L-lactic acid) composite for potential application as an anti-icing material for refrigerator interior walls.
Keywords: candle grease; fly ash; hydrophobicity; petal-like microsphere; phase separation.