This work presents a comparative study related to the photocatalytic efficiency associated with wettability measurements and organic dye degradation, as well as other relevant properties (i.e., corrosion resistance, roughness, wettability, and adhesion to a substrate). The photocatalytic precursors are titanium dioxide nanoparticles (TiO2 NPs) which are dispersed onto a polymeric electrospun fiber matrix by using three different deposition techniques such as electrospraying, spraying, and dip-coating, respectively. In this work, the host electrospun matrix is composed of poly(acrylic acid) fibers crosslinked with cyclodextrin (β-CD), which shows a good chemical affinity and stability with the other deposition techniques which are responsible for incorporating the TiO2 NPs. In order to evaluate the efficacy of each coating, the resultant photocatalytic activity has been monitored by two different tests. Firstly, the reduction in the water contact angle is appreciated, and secondly, the degradation of an organic dye (Rhodamine B) is observed under UV irradiation. In addition, the final roughness, adherence, and pitting corrosion potential have also been controlled in order to determine which solution provides the best combination of properties. Finally, the experimental results clearly indicate that the presence of TiO2 NPs deposited by the three techniques is enough to induce a super hydrophilic behavior after UV irradiation. However, there are notable differences in photocatalytic efficiency on the Rhodamine B as a function of the selected deposition technique.
Keywords: dip coating; electrospraying; photocatalysis; spraying; wettability.