Objectives: To investigate the shrinkage-induced damage at the composite-tooth interface by finite element analysis (FEA) using the cohesive zone model (CZM).
Methods: Axisymmetric models of Class I restorations were created to illustrate the interfacial damage around composite resin restorations of different dimensions, with polymerization shrinkage modeled analogously to thermal shrinkage. The damage to the adhesive interface was determined using a CZM based on the fracture strength and fracture energy. To show the effects of damage, conventional models with perfectly bonded composite resin restorations were created as controls.
Results: The results indicated interfacial damage at the butt-joint cavosurface margin, dentinoenamel junction, and internal line angle. The percentage of damaged interfacial area was found to increase with decreasing diameter for restorations of the same height. For a given diameter, the damage was more severe for restorations of greater depth. The effects of the damage were further illustrated in the model with a restoration of 2-mm diameter and height. The interfacial damage occurred primarily at the internal line angle (83.3 % of all the damaged interfacial area), leading to local stress relief (from 18.3 MPa to 12.8 MPa), but also higher stress at the damage fronts. Greater local shrinkage was found in composites adjacent to the damage.
Significance: The damage mechanics-based CZM is an essential refinement of the FEA to predict interfacial damage and its implications. The extent of damage was found to be greater around restorations with smaller diameters and greater depths. The entire simulation is available via an open-source platform to facilitate further applications in adhesive dentistry.
Keywords: Cohesive zone model; Composite resins; Finite element analysis; Interfacial damage.