Herein, a serial of full cellulose and lignosulfonate derivatives (LS), including sodium lignosulfonate (LSS), calcium lignosulfonate (LSC), lignosulfonic acid (LSA), composite films were generated through dissolving cellulose in reversible carbon dioxide (CO2) ionic liquids solvent system (TMG/EG/DMSO/CO2 solvent system), followed by a facile solution-gelation transition and absorption strategy. The findings indicated that LS aggregated and embedded inside the cellulose matrix via H-bond interaction. The cellulose/LS derivatives composite films showed good mechanical properties which the tensile strength reaches the maximum value of 94.7 MPa in MCC3LSS film. While for the MCC1LSS film, the breaking strain increases to 11.6 %. The outstanding UV shielding effect and high transmittance in the visible region of composite films were also achieved and the shielding performance of the whole UV region (200-400 nm) tended to 100 % for MCC5LSS film. In addition, thiol-ene click reaction was selected as model reaction to verify the UV-shielding performance. It was also found that the oxygen and water vapor barrier performances of composite films were evidently associated with the intense H-bond interaction and tortuous path effect. The OP and WVP of MCC5LSS film were 0 and 6 × 10-3 g·μm/m2·day·kPa, respectively. These outstanding properties make them with great potential for packaging field.
Keywords: CO(2)-based reversible ionic liquids; Cellulose film; Lignosulfonate; New solvents; UV-shielding.
Copyright © 2023 Elsevier B.V. All rights reserved.