Pressure-induced transformations in glassy GeSe2have been studied using the x-ray absorption spectroscopy. Experiments have been carried out at the scanning-energy beamline BM23 (European Synchrotron Radiation Facility) providing a micrometric x-ray focal spot up to pressures of about 45 GPa in a diamond anvil cell. Both Se and Ge K-edge experiments were performed under different hydrostatic conditions identifying the metallization onsets by accurate determinations of the edge shifts. The semiconductor-metal transition was observed to be completed around 20 GPa when neon was used as a pressure transmitting medium (PTM), while this transition was slightly shifted to lower pressures when no PTM was used. Accurate double-edge extended x-ray absorption fine structure (EXAFS) refinements were carried out using advanced data-analysis methods. EXAFS data-analysis confirmed the trend shown by the edge shifts for this disordered material, showing that the transition from tetrahedral to octahedral coordination for Ge sites is not fully achieved at 45 GPa. Results of present high pressure EXAFS experiments have shown the absence of significant neon incorporation into the glass within the pressure range up to 45 GPa.
Keywords: glasses; high pressure; polyamorphism; x-ray absorption spectroscopy.
Creative Commons Attribution license.