In order to solve the problem of environmental pollution caused by the escape of coal dust in open-pit coal mines, a composite dust suppressant was prepared from Enteromorpha, and the preparation factors (water-soluble polymer, temperature, solid content and surfactant) were optimized. The mechanism of dust suppression and the possibility of large-scale field application were discussed. The research results on the related properties of dust suppressants showed that the performance of Enteromorpha-based dust suppressants prepared by this method was excellent compared with similar studies. Among them, polyacrylamide (PAM) Enteromorpha-based dust suppressant had the best performance, with viscosity of 25.1 mPa s and surface tension of 27.05 mN/m. Moreover, PAM Enteromorpha-based dust suppressant had the best effect, with the mass loss of 2.94% under the wind speed of 10 m/s and the coal dust loss rate of 4.6% after rain erosion, and it had strong water retention performance. Through the discussion of dust suppression mechanism, it was found that the mechanical entangled network structure with hydrogen bonds as nodes was formed after the graft copolymerization of PAM and Enteromorpha. It had high permeability and good adhesion. After quickly wetting coal dust, it formed a dense package for coal dust. The field experiment also showed that the use of Enteromorpha-based dust suppressant can effectively inhibit the escape of coal dust. From the point of view of economy and efficiency, Enteromorpha can save 30% of the material cost and the dust suppression efficiency can reach 89-94%. Therefore, the Enteromorpha-based dust suppressant may stably suppress coal dust on the basis of reducing the cost.
Keywords: Coal dust; Enteromorpha; Environment-friendly dust suppressant; Reuse; Water-soluble polymer.
© 2023. The Author(s), under exclusive licence to Springer Nature B.V.