The article presents the results of the synthesis and characteristics of the amphiphilic block terpolymers, built of a hydrophilic polyesteramine block, and hydrophobic blocks made of lactidyl and glycolidyl units. These terpolymers were obtained during the copolymerization of L-lactide with glycolide carried out in the presence of previously produced macroinitiators with protected amine and hydroxyl groups. The terpolymers were prepared to produce a biodegradable and biocompatible material containing active hydroxyl and/or amino groups, with strong antibacterial properties and high surface wettability by water. The control of the reaction course, the process of deprotection of functional groups, and the properties of the obtained terpolymers were made based on 1H NMR, FTIR, GPC, and DSC tests. Terpolymers differed in the content of amino and hydroxyl groups. The values of average molecular mass oscillated from about 5000 g/mol to less than 15,000 g/mol. Depending on the length of the hydrophilic block and its composition, the value of the contact angle ranged from 50° to 20°. The terpolymers containing amino groups, capable of forming strong intra- and intermolecular bonds, show a high degree of crystallinity. The endotherm responsible for the melting of L-lactidyl semicrystalline regions appeared in the range from about 90 °C to close to 170 °C, with a heat of fusion from about 15 J/mol to over 60 J/mol.
Keywords: aliphatic polyester; antibacterial polymer; biodegradable polymer; functional polymer; wettability.