Three-dimensional (3D) printing polymers such as urethane dimethacrylate (UDMA) and ethoxylated bisphenol A dimethacrylate (Bis-EMA) are typically used in definitive prosthesis and require surface treatments before bonding. However, surface treatment and adhesion conditions often affect long-term use. Herein, polymers were divided into Groups 1 and 2 for the UDMA and Bis-EMA components, respectively. The shear bond strength (SBS) between two types of 3D printing resins and resin cements was measured using Rely X Ultimate Cement and Rely X U200, according to adhesion conditions such as single bond universal (SBU) and airborne-particle abrasion (APA) treatments. Thermocycling was performed to evaluate the long-term stability. Sample surface changes were observed using a scanning electron microscope and surface roughness measuring instrument. The effect of interaction between the resin material and adhesion conditions on the SBS was analyzed via a two-way analysis of variance. The optimal adhesion condition for Group 1 was achieved when U200 was used after APA and SBU, whereas Group 2 was not significantly affected by the adhesion conditions. After thermocycling, the SBS significantly decreased in Group 1 without APA treatment and in the entire Group 2. Additionally, porosity, along with increased roughness, was observed on both material surfaces after APA.
Keywords: 3D printing resin; adhesion conditions; shear bond strength; surface roughness; surface treatment; thermocycling.