In order to obtain films with high corrosion resistance and excellent interfacial contact resistance (ICR) on 316L stainless steel used for bipolar plates in proton-exchange membrane fuel cells (PEMFCs), Cr, Ti co-doped amorphous carbon films were prepared on 316L stainless steel. The preparation method for the coating was magnetron sputtering. The doping amount of the Ti element was controlled by a Cr target and a Ti target current. The change in the structure and properties of the coating after the change from Cr single-element doping to Cr and Ti co-doping was studied. The change rule of the structure and properties of the coating from Cr single-element doping to Cr and Ti co-doping was studied. An increase in the Ti content led to a decreased grain boundary, a flatter surface, and a higher sp2-hybridized carbon content. TiC and CrC nanocrystals were formed in the amorphous carbon structure together. The amorphous carbon films doped with Cr and Ti simultaneously achieved a low ICR and high corrosion resistance compared with single-Cr-doped amorphous carbon. The enhanced corrosion resistance was attributed to the decreasing grain boundary, the formation of the TiC crystal structure, and the smaller grain size. The best performance was obtained at a Ti target current of 2A. Compared with bare 316L stainless steel, the corrosion resistance of Cr, Ti co-doped amorphous carbon (Icorr = 5.7 × 10-8 A/cm2, Ti-2 sample) was greatly improved. Because Ti doping increased the content of sp2-hybridized carbon in the coating, the contact resistance of the coating decreased. Moreover, the interfacial contact resistance was 3.1 mΩ·cm2 in the Ti-2 sample, much lower than that of bare 316L stainless steel. After the potentiostatic polarization test, the coating still had excellent conductivity.
Keywords: Cr; Ti co-doped; amorphous carbon films; bipolar plate; corrosion resistance; interfacial contact resistance.