The rapid development of hydrogen fuel cells has been paralleled by increased demand for lightweight type IV hydrogen storage vessels with high hydrogen storage density, which raises the performance requirements of internal plastic liners. An appropriate manufacturing process is important to improve the quality of polymer liners. In this paper, DSC, WAXD, a universal testing machine and a differential pressure gas permeameter were used to investigate the effect of the cooling rate of the rotational molding polyamide 11 on the thermal, crystallization, mechanical and barrier properties. The cooling rate is formulated according to the cooling rate that can be achieved in actual production. The results suggest that two PA11 liner materials initially exhibited two-dimensional (circular) growth under non-isothermal crystallization conditions and shifted to one-dimensional space growth due to spherulite collision and crowding during the secondary crystallization stage. The slower the cooling process, the greater the crystallinity of the specimen. The increase in crystallinity significantly improved the barrier properties of the two PA11 liner materials, and the gas permeability coefficient was 2-3-fold higher than at low crystallinity. Moreover, the tensile strength, the tensile modulus, the flexural strength, and the flexural modulus increased, and the elongation at break decreased as the crystallinity increased.
Keywords: crystallinity; gas barrier properties; polyamide 11; polymer liner of type IV hydrogen storage vessel; rotational molding.