W is a widely used refractory metal with ultra-high melting point up to 3410 °C. However, its applications are limited by poor ablation resistance under high-temperature flame and air flow, which is crucial for aerospace vehicles. To improve the ablation resistance of W under extreme conditions, W-Y alloys doped with different Hf mass fractions (0, 10, 20, and 30) were prepared using the fast hot pressing sintering method. Microstructure and ablation behaviours at 2000 °C were investigated. Results showed that adding an appropriate amount of Hf improved the properties of the W-Y alloy evidently. In particular, the hardness of the alloy increased with the increased content of Hf. The formation of the HfO2 layer on the surface during ablation decreased the mass and linear ablation rates, indicating enhanced ablation resistance. However, excessive Hf addition will result in crack behaviour during ablation. With a Hf content of 20 wt.%, the alloy exhibited high stability and an excellent ablation resistance.
Keywords: HfO2 oxide layer; HfW2; ablation resistance; tungsten-yttrium-hafnium alloy.