Steel fiber-reinforced ultra-high-performance concrete (UHPC) is becoming an important type of concrete reinforcement. After mixing with the reinforced steel fibers, the UHPC has perfect flex resistance, shear strength, crack resistance, shock resistance, and anti-seepage. In this study, the influence of straight, corrugated, and hooked brass-coated steel fibers (BCSFs) on the microstructure, mechanical properties, and crack expansion mechanism of ultra-high-performance concrete (UHPC) with varying content of 1-6 wt.% under different curing times were investigated. Field emission scanning electron microscopy and energy dispersive X-ray spectrometry were employed to characterize the microstructure of the BCSF-reinforced UHPC mix specimens. X-ray computed tomography was employed to determine the porosity of the BCSF-reinforced UHPC mix specimens. The obtained results indicate the flexural strength and compressive strength of BCSF-reinforced UHPC mix specimens are enhanced, along with increasing the content of BCSFs reinforcement with different shapes (straight, corrugated, and hooked). The embedded BCSFs play a major role in the adhesive property and stress transfer of the BCSFs-UHPC matrix interface. Different from many studies, the flexural strength of mix UHPC with straight BCSFs is higher than those with corrugated and hooked BCSFs. However, the compressive strength of UHPC with corrugated BCSFs is higher than those with straight and hooked BCSFs. The flexural strength of mix UHPC with 6 wt.% straight BCSFs at 28 days reaches the maximum value of 26.2 MPa, and the compressive strength of UHPC with 6 wt.% corrugated BCSFs at 28 days reaches the maximum value of 142.3 MPa. With the increase in straight BCSF content from 1 wt.% to 6 wt.%, the porosity in mix UHPC reduces gradually from 18.4% to 8.3%. The length of average crack spacing is dependent on the straight BCSF content. With the increase in straight BCSF content from 1 wt.% to 6 wt.%, the average crack length reduces gradually from 34.2 mm to 12.1 mm, and the average crack width reduces gradually from 0.78 mm to less than 0.1 mm. During crack extension, part of the energy in the UHPC mixture specimen with the 6 wt.% BCSF content flows into the crack tip region converted into the work dissipated during the bridging process. The crack propagation resistance of the UHPC mixture with straight BCSFs was improved compared with those with corrugated and hooked BCSFs. The bond strength between the BCSFs and UHPC matrix was enhanced by using vibrational mixing, and the brass film coated on the BCSFs contributes to increase the flexural and compressive strength of the UHPC mixture.
Keywords: brass-coated steel fibers; compressive strength; crack extension mechanism; flexural strength; microstructure; ultra-high performance concrete.