Objective: Fibrin sealants are routinely used for intra-articular surgical fixation of cartilage fragments and implants. However, the mechanical properties of fibrin sealants in the context of cartilage repair are unknown. The purpose of this study was to characterize the adhesive and frictional properties of fibrin sealants using an ex vivo model.
Design: Native bovine cartilage-bone composites were assembled with a single application of Tisseel or Vistaseal. Composites were tested in tension and lap shear. In addition, the coefficient of friction (COF) was measured in a native cartilage annulus model alone and with minced cartilage. Finally, the effect of a double application of fibrin sealant was evaluated.
Results: There were no significant differences in tensile modulus, ultimate tensile strength (UTS), shear modulus, or ultimate shear strength (USS) between the 2 fibrin sealants. Both fibrin sealants demonstrated a UTS and USS of <8 and <30 kPa, respectively. There were no differences in COF between the sealants when tested alone or with minced cartilage. A double application of fibrin sealant did not alter the mechanical properties compared with a single application of fibrin sealant.
Conclusions: Fibrin sealant adhesive properties are not affected by the sealant type studied or the number of applications in a bovine cartilage-bone model. Fibrin sealant tribological properties are not affected by sealant type or the addition of minced cartilage. The adhesive properties of Tisseel and Vistaseal were less than those desired for the in vivo fixation of cartilage repair implants. These findings motivate the development of an improved cartilage-specific adhesive for cartilage repair applications.
Keywords: Tisseel; Vistaseal; cartilage; fibrin glue; fibrin sealant.