Introduction: This study examined Vickers hardness as well as surface characteristics of different computer-aided design/computer-aided manufacturing (CAD/CAM) resin composites prior to and after storage in various media.
Materials and methods: CAD/CAM resin composite blocks (Grandio Blocs (GB), Lava Ultimate (LU), Brilliant Crios (BC), Cerasmart (GC), Shofu Block HC (SB), Tetric CAD (TC), Luxacam Composite (LC); incl. different translucency variants) were prepared, polished and surface free energy was determined. The specimens were divided into four groups: dry conditions for 24 h (25 °C), demineralized water (37 °C), Pepsi Cola (37 °C) and 75% ethanol (37 °C). After seven and 28 days of storage, Vickers hardness was determined. Surface roughness was measured after the entire storage period.
Results and discussion: Vickers hardness was in the range of about 150 HV for GB, around 115 HV for LU, and 80-100 HV for BC, GC, SB, TC and LC. Only minor differences (total: 50.2 (6.4)-56.2 (3.2) mN/m) in surface free energy could be detected. No relationship was observed between surface free energy and filler content. However, a correlation between filler content and Vickers hardness was evident. Artificial aging caused a decrease of Vickers hardness (up to -40 HV or 35%) depending on storage media, duration and material. The changes in surface texture after immersion in different media were below a value of ΔSa = 0.015 µm.
Conclusion: Artificial aging of CAD/CAM resin composites leads to a significant decrease of Vickers hardness for most materials, while only small changes in surface roughness were identified.
© 2023. The Author(s).