Diabetic wounds with complex pathophysiology significantly burden the wound care industry and require novel management strategies. In the present study, we hypothesized that agarose-curdlan based nanofibrous dressings could be an effective biomaterial for addressing diabetic wounds due to their inherent healing properties. Hence, agarose/curdlan/polyvinyl alcohol based nanofibrous mats loaded with ciprofloxacin (0, 1, 3, and 5 wt%) were fabricated using an electrospinning technique with water and formic acid. In vitro evaluation revealed the average diameter of the fabricated nanofibers between 115 and 146 nm with high swelling (~450-500 %) properties. They exhibited enhanced mechanical strength (7.46 ± 0.80 MPa -7.79 ± 0.007 MPa) and significant biocompatibility (~90-98 %) with L929 and NIH 3T3 mouse fibroblasts. In vitro scratch assay showed higher proliferation and migration of fibroblasts (~90-100 % wound closure) compared to electrospun PVA and control. Significant antibacterial activity was observed against Escherichia coli and Staphylococcus aureus. In vitro real-time gene expression studies with human THP-1 cell line revealed a significant downregulation of pro-inflammatory cytokines (8.64 fold decrease for TNF-α) and upregulation of anti-inflammatory cytokines (6.83 fold increase for IL-10) compared to lipopolysaccharide. In brief, the results advocate agarose-curdlan mat as a potential multifunctional, bioactive, and eco-friendly dressing for healing diabetic wounds.
Keywords: Antibacterial dressings; Benign solvent; Biocompatibility; Enhanced swelling; Immunomodulatory mats; Nanofibrous agarose-curdlan dressings.
Copyright © 2023 Elsevier B.V. All rights reserved.