In recent years, phase change materials (PCMs) have been widely used in waste heat utilization, buildings, and solar and wind energy, but with a huge limitation from the low thermal conductivity, photothermal conversion efficiency, and low latent heat. Organic PCMs are eyecatching because of its high latent heat storage capability and reliability, but they still suffer from a lack of photothermal conversion and sharp stability. Here, we prepared sharp-stable PCMs by establishing a carbon material frame system consisting of graphene oxide (GO) and biochar. In particular, surfactants (CTAB, KH-560 and KH-570) were employed to improve the dispersity of GO in PEG. The differential scanning calorimetry results shows that the latent heat of PEG modified by CTAB grafted GO (PGO-CTAB) was the highest (191.36 J/g) and increased by 18.31% compared to that of pure PEG (161.74 J/g). After encapsulation of PGO-CTAB in biochar, the obtained composite PCM with the amount of biochar and PGO-CTAB in weight ratio 4:6 (PGO-CTAB/CS6(6)) possesses relatively high latent heat 106.51 J/g with good leak resistance and thermal stability, and with obviously enhanced thermal conductivity (0.337 W/(m·K)) and photothermal conversion efficiency (77.43%), which were higher than that of PEG6000 (0.325 W/(m·K), 44.63%). The enhancement mechanism of heat transfer and photothermal conversion on the composite PCM is discussed.
Keywords: biochar; graphene oxide (GO); phase change materials (PCMs); surfactants; the photothermal conversion efficiency; thermal conductivity.