This study aims to explore the radiation protection properties of white mortars based on white cement as a binder and Bi2O3 micro and nanoparticles in proportions of 15 and 30% by weight as replacement sand. The average particle size of micro- and nano-Bi2O3 was measured using a transmission electron microscope (TEM). The cross-sectional morphology and distribution of Bi2O3 within the samples can be obtained by scanning electron microscopy (SEM), showing that nanoscale Bi2O3 particles have a more homogeneous distribution within the samples than microscale Bi2O3 particles. The shielding parameters of the proposed mortars were measured using the HPGe detector at various γ-ray energies emitted by standard radioactive point sources 241Am, 133Ba, 60Co, 137Cs, and 152Eu. The experimental values of the prepared mortars' mass attenuation coefficients (MAC) match well with those determined theoretically from the XCOM database. Other shielding parameters, including half value layer (HVL), tenth value layer (TVL), mean free path (MFP), effective electron density (Neff), effective atomic number (Zeff), equivalent atomic number (Zeq), and exposure buildup factor (EBF), were also determined at different photon energies to provide more shielding information about the penetration of gamma radiation into the selected mortars. The obtained results indicated that the sample containing 30% by weight of nano Bi2O3 has the largest attenuation coefficient value. Furthermore, the results show that the sample with a high concentration of Bi2O3 has the highest equivalent atomic numbers and the lowest HVL, TVL, MFP, and EBF values. Finally, it can be concluded that Bi2O3 nanoparticles have higher efficiency and protection compared to microparticles, especially at lower gamma-ray energies.
Keywords: attenuation coefficients; bismuth oxide; effective atomic number; exposure buildup factor; half value layer; white cement.