Cost reduction in bipolar plates in proton exchange membrane water electrolyzers has previously been attempted by substituting bulk titanium with austenitic stainless steels protected with highly conductive and corrosion-resistant coatings. However, austenitic steels are more expensive than ferritic steels due to their high nickel content. Herein we report on the corrosion resistance of two high chromium ferritic stainless steels, AISI 442 and AISI 446, as an alternative material to manufacture bipolar plates. Electrochemical corrosion tests have shown that AISI 442 and AISI 446 have similar corrosion resistance, while AISI 446 reveals more noble corrosion potential and performs better during potentiostatic stress tests. The current density obtained during polarization at 2 V versus the standard hydrogen electrode (SHE) is 3.3 mA cm-2, which is more than two times lower than on AISI 442. Additionally, surface morphology characterization demonstrates that in contrast to AISI 442, AISI 446 is not sensitive to intercrystalline or pitting corrosion. Moreover, EDX energy dispersion analysis of AISI 446 reveals no differences in the chemical composition of the surface layer compared to the base material, as a confirmation of its high corrosion resistance. The results of this work open up the perspective of replacing austenitic stainless steels with less expensive ferritic stainless steels for the production of components such as bipolar plates in proton exchange membrane water electrolyzers.
Keywords: PEMWE; bipolar plate; corrosion resistance; ferritic stainless steel; water electrolysis.