The radiation-induced photoluminescence (PL) of LiF has found its way into many applications for the detection and imaging of ionizing radiation. In this work, the influence of thermal treatment at temperatures up to 400 °C on absorption and PL emission spectra as well as fluorescent nuclear tracks in irradiated LiF crystals was investigated. It was found that carrying out PL measurements with the crystals kept at the temperature of about 80 °C leads to a considerable increase in luminescence emission of F3+ color centers at 525 nm. This enhancement of PL intensity allows for the microscopic imaging of the fluorescent nuclear tracks using only F3+ emission, which is not possible at room temperature. It was also found that heating the irradiated crystals before measurement at temperatures from 100 °C to 200 °C increases the concentration of F3+ centers. However, the related enhancement of PL emission is insufficient in terms of enabling the observation of the fluorescent tracks in this part of the spectrum. In the case of the main PL emission at 670 nm related to F2 centers, the thermal treatment at around 290 °C substantially increases the intensity of fluorescent tracks. This effect, however, was found to occur only at low fluences of alpha particles (up to about 109 cm-2); therefore, it is barely visible in the emission spectrum and not noticeable in the absorption spectrum.
Keywords: FNTD; color centers; lithium fluoride; photoluminescence; temperature.