The optimum composition ratio of the anode cermet (Ni-GDC) for solid oxide fuel cells (SOFCs) varies because the electron-collecting mechanism is different depending on its applications. A Co-sputtering method facilitates ratio control with sputtering power adjustment. However, there is a practical issue with fabricating anode cermet with various ratios attributed to the large sputtering yield gap of the metal target, Ni, and the ceramic target, gadolinia-doped ceria (GDC). Therefore, in this study, a Gd-Ce metal alloy was applied instead of GDC to match the sputtering rate with that of Ni, which enables a wide ratio range achievement. A thin film of Gd-Ce oxidized after deposition and successfully transformed to crystallized GDC under a SOFC operation environment. X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM) confirmed its crystallinity, and the film deposited with various power ratios was sputtered on the ScSZ electrolyte pellet to clarify the optimum Ni-GDC ratio for thin-film SOFCs. Last, the Ni-GDC was applied to anodized aluminum oxide (AAO)-supported SOFCs to maximize the performance. The performance change according to the thickness of Ni-GDC was identified, and the best performance among them was 638 mW/cm2 at 500 °C.
Keywords: Ni-GDC; anode thickness; low-temperature solid oxide fuel cell; ratio control; sputtering.