Operando Characterization and Theoretical Modeling of Metal|Electrolyte Interphase Growth Kinetics in Solid-State Batteries. Part I: Experiments

Edouard Quérel; Nicholas J Williams; Ieuan D Seymour; Stephen J Skinner; Ainara Aguadero

doi:10.1021/acs.chemmater.2c03130

Operando Characterization and Theoretical Modeling of Metal|Electrolyte Interphase Growth Kinetics in Solid-State Batteries. Part I: Experiments

Chem Mater. 2023 Jan 20;35(3):853-862. doi: 10.1021/acs.chemmater.2c03130. eCollection 2023 Feb 14.

Authors

Edouard Quérel¹, Nicholas J Williams¹, Ieuan D Seymour¹, Stephen J Skinner¹, Ainara Aguadero^{1

2}

Affiliations

¹ Department of Materials, Imperial College London, Exhibition Road, LondonSW7 2AZ, U.K.
² Instituto de Ciencia de Materiales de Madrid, ICMM-CSIC, Sor Juana Ines de La Cruz 3, 28049Madrid, Spain.

Abstract

To harness all of the benefits of solid-state battery (SSB) architectures in terms of energy density, their negative electrode should be an alkali metal. However, the high chemical potential of alkali metals makes them prone to reduce most solid electrolytes (SE), resulting in a decomposition layer called an interphase at the metal|SE interface. Quantitative information about the interphase chemical composition and rate of formation is challenging to obtain because the reaction occurs at a buried interface. In this study, a thin layer of Na metal (Na⁰) is plated on the surface of an SE of the NaSICON family (Na_3.4Zr₂Si_2.4P_0.6O₁₂ or NZSP) inside a commercial X-ray photoelectron spectroscopy (XPS) system while continuously analyzing the composition of the interphase operando. We identify the existence of a solid electrolyte interphase at the Na⁰|NZSP interface, and more importantly, we demonstrate for the first time that this protocol can be used to study the kinetics of interphase formation. A second important outcome of this article is that the surface chemistry of NZSP samples can be tuned to improve their stability against Na⁰. It is demonstrated by XPS and time-resolved electrochemical impedance spectroscopy (EIS) that a native Na _x PO _y layer present on the surface of as-sintered NZSP samples protects their surface against decomposition.