To obtain high-efficiency solution-processed organic light-emitting diodes (OLEDs), a hole transport material (HTM) capable of solution processing with excellent charge transport properties is required. In this study, a new vinyl polymer (PmCP) containing hole-transporting 1,3-di(9H-carbazol-9-yl)benzene (mCP) in the side chain was successfully synthesized via radical polymerization. PmCP showed good film-forming ability and thermal stability. Moreover, PmCP has a higher triplet energy value and hole mobility than poly(N-vinylcarbazole) (PVK) used as a reference HTM, which can be applied as a hole transport layer (HTL) in thermally activated delayed fluorescence (TADF) OLEDs, providing green and blue emissions. PmCP-based solution-processable TADF-OLEDs containing green- and blue-emitting layers were easily fabricated without damaging the lower HTL while using ethyl acetate as an orthogonal solvent. The corresponding OLEDs possess high external quantum efficiencies of 29.60% and 11.00% for the green- and blue-emitting devices, respectively. They show superior performances compared to PVK-based devices used as a reference. It was confirmed that PmCP as a solution-processable HTM can replace PVK and is universally applicable to both green- and blue-emitting devices.
Keywords: green and blue emission; hole transporting polymer; organic light-emitting diode; solution process; thermally delayed fluorescence.