Absorption-dominated electromagnetic interference (EMI) shielding is attained by improving impedance matching and conductivity through structural design. Polyvinylidene fluoride (PVDF)-Ti3C2Tx MXene-single-walled carbon nanotubes (SWCNTs) composites with layered heterogeneous conductive fillers and segregated structures were prepared through electrostatic flocculation and hot pressing of the PVDF composite microsphere-coated MXene and SWCNTs in a layer-by-layer fashion. Results suggest that the heterogeneous fillers improve impedance matching and layered coating, and hot compression allows the MXene and SWCNTs to form a continuous conducting network at the PVDF interface, thereby conferring excellent conductivity to the composite. The PVDF-MXene-SWCNTs composite showed a conductivity of 2.75 S cm-1 at 2.5% MXene and 1% SWCNTs. The EMI shielding efficiency (SE) and contribution from absorption loss to the total EMI SE of PVDF-MXene-SWCNTs were 46.1 dB and 85.7%, respectively. Furthermore, the PVDF-MXene-SWCNTs composite exhibited excellent dielectric losses and impedance matching. Therefore, the layered heteroconductive fillers in a segregated structure optimize impedance matching, provide excellent conductivity, and improve absorption-dominated electromagnetic shielding.
Keywords: MXene; electromagnetic interference shielding; polyvinylidene fluoride; segregated structure; single-walled carbon nanotubes.