Wrought magnesium alloys have received attention due to their potential application as lightweight materials. However, their use is limited by their poor corrosion resistance. Rare earth additions have the potential to enhance corrosion resistance. The present work included a microstructural investigation and corrosion testing of the alloy WE-43, containing Nd and Y, which was compared against the more conventional compositions of AZ31 and AZ61 alloys. All three alloys exhibited a recrystallized equiaxed structure after hot rolling with the presence of second phases-precipitates. The WE-43 alloy exhibited a better corrosion resistance than AZ31 and AZ61 under salt fog testing, indicated by the lower depth of attack and lower weight loss. The second phases in the microstructure of AZ31 and AZ61 alloys determined their corrosion resistance. The second phases in the AZ31 and AZ61 alloys (based on Al-Mg and Al-Mn phases) were nobler than the Mg matrix and catholically acted, thus sacrificing the Mg matrix. The superior corrosion resistance of WE43 was due to the incorporation of Y in the oxide/hydroxide film. In addition, the second phases in the WE43 consisted of Nd and Y and were less noble than the Mg-matrix. Thus, they acted as anodic sites protecting the Mg-matrix. The above results show the beneficial effect of rare earth additions to wrought Mg alloys towards increased corrosion resistance.
Keywords: AZ31; AZ61; WE43; XPS; corrosion; magnesium alloys; microstructure; rare earth elements; weight loss.