The development of active packaging based on biodegradable material and incorporating active compounds, such as essential oil, is a new technique to ensure food safety without harming the environment. In this study, nanofiber mats of poly (lactic acid)/ polyethylene glycol (PLA/PEG) blend incorporated with peppermint essential oil (PO) at different ratios (5-20 % v/w) were produced by solution-blow-spinning (SBS) for potential packaging application. Electron microscopy showed a cylindrical and interlaced morphology for PLA/PEG/PO and a significant increase in the diameter (139-192 nm) of the nanofibers by increasing PO content. All nanofibers showed high thermal stability (278-345 °C) suitable for use in the food industry. Nuclear magnetic resonance (13C NMR) spectrum confirmed PO in the nanofibers after SBS. ATR-FTIR spectral analysis supported the chemical composition of the nanofiber mats. PO addition led to obtaining hydrophobic nanofibers, enhancing the contact angle to 122° and decreasing water vapor permeability (60 % reduction compared to the PLA/PEG (3.0 g.mm.kPa-1.h-1.m-2). Although the PLA/PEG/20%PO nanofibers did not show halo formation in 24 h, they effectively extended the strawberries' shelf-life at 25 °C, evidencing PO release over time. It also reduced weight loss (2.5 % and 0.3 % weight loss after 5 days for PLA/PEG and PLA/PEG/20%PO, respectively) and increased firmness (8-12 N) for strawberries packed with the nanofiber mats. It is suggested that PLA/PEG films incorporating PO may be used as an active, environmentally friendly packaging material.
Keywords: Antioxidant activity; Food packaging; Fruit preservation.
Copyright © 2023 Elsevier B.V. All rights reserved.