Objective: To analyze simplified adhesive containing pure or silanized bioglass 45S5 (with calcium) or Sr-45S5 (strontium-substituted) fillers applied on dentin and to evaluate the microtensile bond strength (µTBS), interface nanoleakage, degree of conversion of adhesive, collagen degradation and remineralization.
Methods: Ambar Universal adhesive (FGM) was doped with 10 wt% bioactive glasses to form following groups: Control (no bioglass), 45S5 (conventional bioglass 45S5), Sr-45S5 (Sr-substituted bioglass 45S5), Sil-45S5 (silanized bioglass 45S5) and Sil-Sr-45S5 (silanized bioglass Sr-45S5). Adhesives were applied after dentin acid-etching using phosphoric acid at extracted human molars. Resin-dentin sticks were obtained and tested for µTBS, nanoleakage at 24 h or 6 months. Degree of conversion was measured using micro-Raman spectroscopy. Dentin remineralization was assessed by FTIR after 6-month storage in PBS. Hydroxyproline (HYP) release was surveyed by UV-Vis spectroscopy. Statistical analysis was performed using ANOVA and Tukey's test (p < 0.05).
Results: Regarding µTBS, Sr-45S5 and 45S5 presented higher and stable results (p > 0.05). Control (p = 0.018) and Sil-Sr-45S5 (p < 0.001) showed µTBS reduction after 6-month aging. Sil-Sr-45S5 showed higher HYP release than that obtained in the 45S5 group. Sil-45S5 showed mineral deposition and increase in µTBS (p = 0.028) after 6-months. All experimental adhesives exhibited higher degree of conversion compared to Control group, except for 45S5. All adhesives created gap-free interfaces, with very low silver impregnation, except for Sil-Sr-45S5.
Significance: The incorporation of silanized 45S5 bioglass into the universal adhesive was advantageous in terms of dentin remineralization, bonding performance and adhesive polymerization. Conversely, Sil-Sr-45S5 compromised the µTBS, interface nanoleakage and had a negative impact on HYP outcomes.
Keywords: Bioglass; Dentin; Remineralization; Silanization; Strontium.