Laminated composites have been commonly applied to all fields. When made into laminated composites, Kevlar woven fabrics are able to provide the required functions. In this study, two types of TPU are incorporated to improve the intralayer features of Kevlar/TPU laminated composites. Hence, the Kevlar/TPU laminated composites consist of firmly bonded laminates while retaining flexibility of the fabrics. Being the interlayer of the laminated composites, the TPU layer provides adhesion while strengthening the tensile property, dynamic puncture resistance, and buffer strength of Kevlar/TPU laminated composites. The test results indicate that with a blending ratio of two types of TRU being 85/15 wt%, the Kevlar/TPU laminated composites exhibit a tensile strength of 18.08 MPa. When the stacking thickness is 1 mm, the tensile strength is improved to 357.73 N with the buffering strength reaching 4224.40 N. Notably, with a thickness being 1.2 mm, the laminated composites demonstrate a dynamic resistance being 672.15 N. In the meanwhile, functional Kevlar fabrics are allowed to keep the fiber morphology owing to the protection of TPU composite films. Considering the composition of protective gear, Kevlar/TPU laminated composites possess a powerful potential and are worthwhile exploring.
Keywords: Kevlar; TPU; flexibility; laminated composites.