Ciprofloxacin (CIP) is a commonly used antibiotic, however, once in the environment, it is highly toxic with a poor biodegradability. Given these attributes, an effective strategy for the removal of CIP is urgently needed for the protection of water resources. Herein, a novel copper metal-organic framework (CuxO/MOF) multifunctional material has been produced, in this work, by the calcination of Cu-MOF urea at 300 °C, in the presence of a 5% H2 atmosphere. The morphological, structural, and thermal properties of the prepared CuxO/MOF were determined through various techniques, and its photocatalytic behavior was investigated for the degradation of CIP under visible-light irradiation. The prepared CuxO/MOF bifunctional material is presented as a graphitic carbon-layered structure with a particle size of 9.2 ± 2.1 nm. The existence of CuO-Cu2O-C, which was found on the CuxO/MOF surface, enhanced the adsorption efficiency and increased the photosensitivity of CuxO/MOF, towards the degradation of CIP in aqueous solutions. The tailored CuxO/MOF, not only shows an excellent CIP degradation efficiency of up to 92% with a constant kinetic rate (kobs) of 0.048 min−1 under visible light, but it can also retain the stable photodegradation efficiency of >85%, for at least six cycles. In addition, CuxO/MOF has an excellent adsorption capacity at pH 6.0 of the maximum Langmuir adsorption capacity of 34.5 mg g−1 for CIP. The results obtained in this study demonstrate that CuxO/MOF is a reliable integrated material and serves as an adsorbent and photocatalyst, which can open a new pathway for the preparation of visible-light-responsive photocatalysts, for the removal of antibiotics and other emerging pollutants.
Keywords: CuxO/MOF; adsorption; ciprofloxacin; copper metal organic framework; photodegradation.