The study aims to investigate the adhesion of a hydrogel made of cross-linked low-methyl esterified pectin to rat intestinal serosa ex vivo. The adhesivity of the FeP hydrogel, which was cross-linked by Fe3+ cations, exceeded that of hydrogels cross-linked by Ca2+, Zn2+, and Al3+ cations. The concentration of the cross-linking cation failed to influence the adhesion of the pectin hydrogel to the serosa. The mechanical properties and surface microrelief of the pectin hydrogel were influenced by the type and concentration of the cross-linking cations. Fe3+ cations form a harder and more elastic gel than Ca2+ cations. Scanning electron microscopy analysis revealed the characteristic surface pattern of FeP hydrogel and its denser internal structure compared to Ca2+ cross-linked hydrogel. The effect of the salt composition of the adhesion medium was shown since the FeP hydrogel's adhesion to the serosa was lower in physiological solutions than in water, and adhesion in Hanks' solution was higher than in phosphate buffered saline. Serum proteins and peritoneal leukocytes did not interfere with the serosal adhesion of the FeP hydrogel. Pre-incubation in Hanks' solution for 24 h significantly reduced the adhesion of the FeP hydrogel to the serosa, regardless of the pH of the incubation. Thus, serosal adhesion combined with excellent stability and mechanical properties in physiological environments appeared to be advantages of the FeP hydrogel, demonstrating it to be a promising bioadhesive for tissue engineering.
Keywords: Fe3+ ions; adhesion medium; apple pectin; bioadhesion; hydrogel; mechanical properties; scanning electron microscopy; serosa.