Because of limited self-healing ability, the treatment of articular cartilage defects is still an important clinical challenge. Hydrogel-based biomaterials have broad application prospects in articular cartilage repair. In this study, gelatin methacrylate (GelMA)and silk fibroin (SF) were combined to form a composite hydrogel with an interpenetrating network (IPN) structure under ultraviolet irradiation and ethanol treatment. Introducing silk fibroin into GelMA hydrogel significantly increased mechanical strength as compressive modulus reached 300 kPa in a GelMA/SF-5 (50 mg/mL silk fibroin) group. Moreover, composite IPN hydrogels demonstrated reduced swelling ratios and favorable biocompatibility and supported chondrogenesis of bone mesenchymal stem cells (BMSCs) at day 7 and day 14. Additionally, significantly higher gene expressions of Col-2, Acan, and Sox-9 (p < 0.01) were found in IPN hydrogel groups when compared with the GelMA group. An in vivo study was performed to confirm that the GelMA-SF IPN hydrogel could promote cartilage regeneration. The results showed partial regeneration of cartilage in groups treated with hydrogels only and satisfactory cartilage repair in groups of cell-seeded hydrogels, indicating the necessity of additional seeding cells in hydro-gel-based cartilage treatment. Therefore, our results suggest that the GelMA/SF IPN hydrogels may be a potential functional material in cartilage repair and regeneration.
Keywords: articular cartilage; hydrogel; interpenetrated network; osteochondral defect.