Rapid biosynthesis and characterization of metallic gold nanoparticles by olea europea and their potential application in photoelectrocatalytic reduction of 4-nitrophenol

Salma S Syed; Liyamol Jacob; G Bharath; Mohammed Abu Haija; Anupama Kaushik; Fawzi Banat

doi:10.1016/j.envres.2023.115280

Rapid biosynthesis and characterization of metallic gold nanoparticles by olea europea and their potential application in photoelectrocatalytic reduction of 4-nitrophenol

Environ Res. 2023 Apr 1:222:115280. doi: 10.1016/j.envres.2023.115280. Epub 2023 Jan 16.

Authors

Salma S Syed¹, Liyamol Jacob², G Bharath³, Mohammed Abu Haija⁴, Anupama Kaushik⁵, Fawzi Banat⁶

Affiliations

¹ Department of Chemical Engineering, Khalifa University of Science and Technology, P. O. Box: 2533, Abu Dhabi, United Arab Emirates.
² Department of Mechanical and Materials Engineering, Khalifa University of Science and Technology, P. O. Box: 2533, Abu Dhabi, United Arab Emirates.
³ Department of Chemical Engineering, Khalifa University of Science and Technology, P. O. Box: 2533, Abu Dhabi, United Arab Emirates; Department of Chemistry, Khalifa University of Science and Technology, P. O. Box: 2533, Abu Dhabi, United Arab Emirates.
⁴ Department of Chemistry, Khalifa University of Science and Technology, P. O. Box: 2533, Abu Dhabi, United Arab Emirates.
⁵ Dr. SSB University Institute of Chemical Engineering and Technology, Panjab University, India.
⁶ Department of Chemistry, Khalifa University of Science and Technology, P. O. Box: 2533, Abu Dhabi, United Arab Emirates. Electronic address: fawzi.banat@ku.ac.ae.

PMID: 36657593
DOI: 10.1016/j.envres.2023.115280

Abstract

In recent years, photoelectrocatalysis of gold nanoparticles (Au NPs) has received considerable attention due to their potential to improve catalytic efficiency. Herein, ultra-small Au NPs were successfully synthesized in a single pot using olea europea leaf extract as a green reducing agent for the degradation of 4-nitrophenol. The TEM images showed uniform distribution and spherical shape of Au NPs with an average diameter of 5 nm. Taking advantage of the ability of Au nanoparticles to absorb visible and near-infrared light, 4-nitrophenol can be successfully reduced in the presence of NaBH₄. Additionally, the electrochemical activity of the fabricated Au photocathode was investigated by linear sweep voltammetry in the dark and at VIS-NIR light irradiation. This showed an increased photocurrent density of 27 mA cm^-2 with an onset potential of -0.71 V. This indicates that the Au photocathode is highly active at VIS-NIR light. Interestingly, the Au photocathode showed a higher current density of 37 mA cm^-2 with an onset potential of -0.6 V in the presence of 4-nitrophenol during VIS-NIR irradiation, indicating that 4-nitrophenol was efficiently reduced by the photocathode. The Au photocathode completely reduced 4-nitrophenol in the wastewater within 35 min. Recyclability studies showed that the Au NPs photocathode exhibited higher stability over multiple cycles, confirming the ability of the electrode to treat wastewater over a longer period of time. This study demonstrates the effectiveness of the photoelectrochemical (PEC) process in reducing organic compounds in wastewater.

Keywords: 4-NP reduction; Green synthesis; Olea europea leaf Extract; Photoelectrocatalysts; Wastewater treatment.

Publication types

Research Support, Non-U.S. Gov't

MeSH terms

Gold / chemistry
Metal Nanoparticles* / chemistry
Olea*
Wastewater

Substances

Gold
4-nitrophenol
Wastewater