Bandgap tunable lanthanum niobium oxynitride [LaNb2 O7-x Nx ](1+x)- nanosheet is prepared by the delamination of a Ruddlesden-Popper phase perovskite oxynitride via ion-exchange and two-step intercalation processes. The lanthanum niobium oxynitride nanosheets have a homogeneous thickness of 1.6 nm and exhibit a variety of chromatic colors depending on the nitridation temperature of the parent-layered oxynitride. The bandgap energy of the nanosheets is determined by ultraviolet photoemission spectroscopy, Mott-Schottky, and photoelectrochemical measurements and is found to be tunable in the range of 2.03-2.63 eV. Furthermore, the oxide/oxynitride superlattice structures are fabricated by face-to-face stacking of 2D crystals using oxynitride [LaNb2 O7-x Nx ](1+x)- and oxide [Ca2 Nb3 O10 ]- nanosheets as building blocks. Moreover, the superlattices-like restacked oxynitride/oxide nanosheets hybrid exhibits unique proton conductivity and dielectric properties strongly influenced by the oxynitride nanosheets and enhanced photocatalytic activity under visible light irradiation.
Keywords: 2D oxynitrides; bandgap; dielectric properties; photocatalytic properties; proton conductivity.
© 2023 Wiley-VCH GmbH.