Infection associated with biomedical implants remains the main cause of failure, leading to reoperation after orthopedic surgery. Orthopedic infections are characterized by microbial biofilm formation on the implant surface, which makes it challenging to diagnose and treat. One potential method to prevent and treat such complications is to deliver a sufficient dose of antibiotics at the onset of infection. This strategy can be realized by coating the implant with thermoregulatory polymers and triggering the release of antibiotics during the acute phase of infection. We developed a multi-layered temperature-responsive polymer brush (MLTRPB) coating that can release antibiotics once the temperature reaches a lower critical solution temperature (LCST). The coating system was developed using copolymers composed of diethylene glycol methyl ether methacrylate and 2-hydroxyethyl methacrylate by alternatively fabricating monomers layer by layer on the titanium surface. LCST was set to the temperature of 38-40 °C, a local temperature that can be reached during infection. The antibiotic elution characteristics were investigated, and the antimicrobial efficacy was tested against S. aureus species (Xen29 ATCC 29 213) using one to four layers of MLTRPB. Both in vitro and in vivo assessments demonstrated preventive effects when more than four layers of the coating were applied, ensuring promising antibacterial effects of the MLTRPB coating.
Keywords: antibiotics coating; bacterial biofilm; controlled release; lower critical solution temperature; periprosthetic joint infection; rodent model; smart coating; thermo-responsive.