The Ti6Al4V alloy has been widely used in aerospace equipment and medical devices. However, the poor wear resistance of the Ti6Al4V alloy hinders its further engineering application. In this study, the ultrasonic strengthening grinding process (USGP) and laser texturing process were employed to enhance the wear resistance of Ti6Al4V alloy. The frictional behavior of all samples was determined via a ball-on-disc friction and wear tester under dry conditions. The worn surface morphology, cross-sectional hardness, surface roughness, and microstructure were analyzed. The results demonstrated that the USGP induced high hardness, high dislocation density, and grain refinement, as well as improvements in the wear resistance of Ti6Al4V. Moreover, laser texture could enhance the capacity to capture wear debris and reduce wear probability. When combining the USGP and laser texturing process for the surface treatment of Ti6Al4V alloy, the lowest and most stable friction coefficients were obtained, as well as the best wear resistance. Compared to the polished sample, the steady stage friction coefficient of the sample treated by USGP and laser texturing process was remarkably decreased by 58%. This work demonstrates that combining the USGP and laser texturing process could be a promising solution for improving the wear resistance properties of Ti6Al4V alloy, which makes it more suitable for various engineering applications.
Keywords: Ti6Al4V alloy; laser texture; ultrasonic strengthening grinding process; wear resistance.