Damage analysis of retrieved BioloxⓇdelta components used in hard and soft bearings

Abstract

This retrieval study included 43 Biolox delta explants (18 CoC, 25 CoP). Implants were examined macroscopically, whereby damage was evaluated using a semi quantitative scoring system. Confocal microscopy was used to examine wear related damage patterns of the articulating surfaces. Scanning electron microscopy (SEM) with energy-dispersive X-ray spectroscopy (EDS) was used to analyze wear marks on the implant surface and wear debris in periprosthetic tissue samples. Raman spectroscopy and X-ray diffraction (XRD) were used to quantify monoclinic zirconia fractions. On all components, in vivo wear resulted predominantly in different damage patterns caused by metal transfer. In CoC bearings stripe wear was additionally detected, and some implants underwent severe damage due to component breakage. The wear scores were higher for CoC components, with no differences between the scores for CoC heads and liners. Wear features caused comparable roughening on implants from CoC and CoP bearings. SEM studies demonstrated that most wear marks were caused by metal debris released from implant components. Grain pull-out was observed in stripe wear regions. Monoclinic phase shift was observed in a similar quantity on components from CoP and CoC bearings. The increase of monoclinic zirconia content around metal deposits was minimal and was more pronounced in areas of stripe wear. The results of this study indicate, that ZTA components in general undergo minimal wear in both, CoC and CoP bearings, however, it is more pronounced in the former. Metal deposits, as the most common wear feature, have no significant effect on monoclinic phase transition. STATEMENT OF SIGNIFICANCE: In this paper, we classify all damage patterns macroscopically according to an established scoring system and assess them regarding surface roughness (confocal microscopy) and monoclinic phase content (Raman spectroscopy) in order to derive the severity for patients. We compare hard-hard and hard-soft bearings and relate damage patterns with metal transfer based on SEM/EDS examinations. Furthermore, we work out correlations between patient-specific data, cause of revision and the physical condition of each individual sample Our cohort consists of 43 Biolox delta retrievals, a comparatively large quantity. In addition, we address current topics such as metal transfer and, based on the classification of damage patterns, provide incentives and/or meaningful focal points for further research.