Effects of Er: YAG, Er,Cr: YSGG, and Nd: YAG laser irradiation and adhesive systems on the immediate and long-term bond strength of dentin: a systematic review and meta-analysis

Abstract

At present, lasers are increasingly used in the oral clinical field, and research and applications in dental hard tissue treatment are also increasing. The effect of laser etching dentin on the bonding strength of composite resin reported in the literature is still inconclusive. The purpose of this review was to evaluate whether laser etching can improve the immediate and long-term bonding strength of dentin and investigate the effect of different types of adhesives on the bonding strength of dentin. Two reviewers performed a literature search up from January 2012 to November 2021 in four databases: MEDLINE (PubMed), Web of Science, EMBASE, and the Cochrane Library. A total of 25 studies were included in the meta-analysis. The Cochrane Collaboration Bias Risk Assessment tool was used to evaluate the quality of the included literature, and an analysis was carried out using Review Manager Software version 5.3. The aging bond strength of dentin after erbium (Er): yttrium aluminum garnet (YAG) laser treatment was significantly lower than that of dentin in the bur group (P < 0.00001). At the same time, the bond strength of dentin immediately and aging after (Er), chromium-doped (Cr): yttrium scandium gallium garnet (YSGG) laser treatment was lower than that of dentin in the bur group (P < 0.05). There was no significant difference in the immediate and aging bonding strength among samples in the Er: YAG laser, Er, Cr: YSGG laser, and blank control groups (no laser or bur). The aging bond strength of samples after neodymium-doped (Nd): YAG laser treatment was higher than that of samples in the blank control group (P < 0.05); in addition, the performance of self-etching adhesive was slightly better than that of acid etching adhesive. Regardless of the applied surface treatment and the adhesive employed, dentin after aging showed significant bond degradation (P < 0.05). There was high heterogeneity of bond strength between different groups, and the small number of studies and the contradictory results may be the main reasons for this outcome.

Keywords: Dentin bond strength; Laser treatment; Meta-analysis; Systematic review.