Origanum vulgare manganese ferrite nanocomposite: An advanced multifunctional hybrid material for dye remediation

Abstract

The purpose of the study was to fabricate sustainable and cost-effective material for the thorough cleansing of polluted water. In this context, an economical, phytogenic and multifunctional Origanum vulgare plant-based nanocomposite material, MnFe₂O₄/OV, was prepared via one-pot synthetic technique. The synthesized nanocomposite with a band gap of 2.02 eV behaved as an efficient nano-photocatalyst for the degradation of both cationic (crystal violet) and anionic (congo red) dyes under direct sunlight irradiation. The material also inhibited the growth of E. coli and S. aureus bacteria and simultaneously adsorbed both cationic and anionic dyes from water through adsorption. A variety of techniques have been used to characterize the nanocomposite, including X-ray powder diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX) and transmission electron microscopy (TEM). Additionally, the kinetics of photodegradation of the aforementioned organic dyes has also been investigated. The MnFe₂O₄/OV exhibited excellent photocatalytic performance, leading to 43% and 72% degradation within 3 h at rate constants of 2.0 × 10^-3 min^-1 and 6.0 × 10^-3 min^-1 for crystal violet and congo red, respectively. The crystal violet and congo red were used to testify to the composite's potential for adsorption under the influence of several process variables, including initial solution pH, contact time, temperature, initial dye concentration, and amount of MnFe₂O₄/OV. The Langmuir maximum adsorption capacity Q_max as in the range 14.06-14.59 mgg^-1 for crystal violet and 34.45-23.93 mgg^-1 for congo red at pH 7 within 90 min contact time in the temperature range of 30-50 °C. The phenomenon of adsorption was found feasible and endothermic at all the investigated temperatures. Also, E. coli and S. Aureus bacteria have shown growth suppression activity when exposed to MnFe₂O₄/OV.As a result, the synthesized nanocomposite, MnFe₂O₄/OV, proved to be an antimicrobial, multifunctional novel nanocomposite, which is in high demand, and could serve as an affordable, and sustainable material for comprehensive water filtration.

Keywords: Adsorption; Antibacterial; Congo Red; Crystal violet; Manganese ferrite; Origanum vulgare; Photodegradation.