All-solid-state batteries are appealing electrochemical energy storage devices because of their high energy content and safety. However, their practical development is hindered by inadequate cycling performances due to poor reaction reversibility, electrolyte thickening and electrode passivation. Here, to circumvent these issues, we propose a fluorination strategy for the positive electrode and solid polymeric electrolyte. We develop thin laminated all-solid-state Li||FeF3 lab-scale cells capable of delivering an initial specific discharge capacity of about 600 mAh/g at 700 mA/g and a final capacity of about 200 mAh/g after 900 cycles at 60 °C. We demonstrate that the polymer electrolyte containing AlF3 particles enables a Li-ion transference number of 0.67 at 60 °C. The fluorinated polymeric solid electrolyte favours the formation of ionically conductive components in the Li metal electrode's solid electrolyte interphase, also hindering dendritic growth. Furthermore, the F-rich solid electrolyte facilitates the Li-ion storage reversibility of the FeF3-based positive electrode and decreases the interfacial resistances and polarizations at both electrodes.
© 2022. The Author(s).