In this study, a simple approach was described to investigate the theoretical models for electrospun polymer nanofiber-reinforced nanocomposites. For predicting the tensile strength of the electrospun nylon 6 nanofiber-reinforced polyurethane acrylate composites, conventional Pukanszky, Nicolais-Narkis, Halpin-Tsai, and Neilson models were used, while for Young's modulus, Halpin-Tsai, modified Halpin-Tsai, and Hui-Shia models were used. As per the Pukanszky model, composite films showed better interaction since the values of the interaction parameter, B, were more than 3. Similarly, the value of an interfacial parameter, K, was less than 1.21 (K = -5, for the curve fitting) as per the Nicolais-Narkis model, which indicated better interfacial interaction. For composite films, the modified Halpin-Tsai model was revised again by introducing the orientation factor, α, which was 0.333 for the randomly oriented continuous nanofiber-reinforced composites, and the exponential shape factor, ξ = (2l/d)e-avf-b, which showed the best agreement with the experimental Young's modulus results. Based on mentioned remarks, these models would be applicable for estimating the tensile strength and Young's modulus of electrospun nanofiber-reinforced polymer composite films.
Keywords: electrospinning; mechanical properties; modeling; nanocomposites; nanofiber-reinforced composites.