The efficiency of the removal of Cs-137 radionuclides with porous and non-porous resorcinol−formaldehyde resins from alkaline solutions simulating the composition of real liquid radioactive waste (LRW) streams has been evaluated. Resins were synthesized through the polycondensation of resorcinol and formaldehyde in an alkaline medium at a molar ratio of 1.8/2.2 and a temperature of 210 °C. The Cs-137 distribution coefficients on RFRs in alkaline solutions simulating LRW were above 103 mL/g under static sorption conditions. In a model solution with pH 11, the full dynamic sorption capacity of non-porous RFR was 0.178 mmol/g. The values of the full dynamic sorption capacities of porous RFRs were 0.274 and 1.035 mmol/g for resins obtained with calcium carbonate and toluene as templates, respectively. When the sizes of RFR beads increased two-fold, the volume until 5% cesium breakthrough decreased by 20−40%. The most pronounced beneficial effect of the RFR’s porosity was observed at flow rates from 25 to 50 BV/h. It was shown that the negative effect of metal cations on Cs-137 uptake increases in the following order: Na+ < Mg2+ < Ca2+ < K+. The number of bed volumes of LRW-simulating solution decontaminated with RFRs until 5% cesium breakthrough was above 450; that is higher than the value of known commercially available analogs. The latter shows that the developed RFRs are promising for application in technological schemes of alkaline LRW processing.
Keywords: adsorption; cesium; liquid radioactive waste; resorcinol–formaldehyde resin.