We demonstrated the performance of an Al2O3/SiO2 stack layer AlGaN/GaN metal−oxide semiconductor (MOS) high-electron-mobility transistor (HEMT) combined with a dual surface treatment that used tetramethylammonium hydroxide (TMAH) and hydrochloric acid (HCl) with post-gate annealing (PGA) modulation at 400 °C for 10 min. A remarkable reduction in the reverse gate leakage current (IG) up to 1.5×10−12 A/mm (@ VG = −12 V) was observed in the stack layer MOS-HEMT due to the combined treatment. The performance of the dual surface-treated MOS−HEMT was significantly improved, particularly in terms of hysteresis, gate leakage, and subthreshold characteristics, with optimized gate annealing treatment. In addition, an organized gate leakage conduction mechanism in the AlGaN/GaN MOS−HEMT with the Al2O3/SiO2 stack gate dielectric layer was investigated before and after gate annealing treatment and compared with the conventional Schottky gate. The conduction mechanism in the reverse gate bias was Poole−Frankel emission for the Schottky-gate HEMT and the MOS−HEMT before annealing. The dominant conduction mechanism was ohmic/Poole-Frankel at low/medium forward bias. Meanwhile, gate leakage was governed by the hopping conduction mechanism in the MOS−HEMT without gate annealing modulation at a higher forward bias. After post-gate annealing (PGA) treatment, however, the leakage conduction mechanism was dominated by trap-assisted tunneling at the low to medium forward bias region and by Fowler−Nordheim tunneling at the higher forward bias region. Moreover, a decent product of maximum oscillation frequency and gate length (fmax × LG) was found to reach 27.16 GHz∙µm for the stack layer MOS−HEMT with PGA modulation. The dual surface-treated Al2O3/SiO2 stack layer MOS−HEMT with PGA modulation exhibited decent performance with an IDMAX of 720 mA/mm, a peak extrinsic transconductance (GMMAX) of 120 mS/mm, a threshold voltage (VTH) of −4.8 V, a higher ION/IOFF ratio of approximately 1.2×109, a subthreshold swing of 82 mV/dec, and a cutoff frequency(ft)/maximum frequency of (fmax) of 7.5/13.58 GHz.
Keywords: Al2O3/SiO2; AlGaN/GaN; MOS-HEMT; post-gate annealing (PGA).