Dual-phase low-alloy steels combine a soft ferrite phase with a hard martensite phase to create desirable properties in terms of strength and ductility. Nickel additions to dual-phase low-alloy steels can increase the yield strength further and lower the transformation temperatures, allowing for microstructure refining. Determining the correct intercritical annealing temperature as a function of nickel content is paramount, as it defines the microstructure ratio between ferrite and martensite. Likewise, quantifying the influence of nickel on the intercritical temperature and its synergistic effect with the microstructure ratio on mechanical properties is vital to designing dual-phase steels suitable for corrosive oil and gas services as well as hydrogen transport and storage applications. In this work, we used a microstructural design to develop intercritical annealing heat treatments to obtain dual-phase ferritic-martensitic low-alloy steels. The intercritical annealing and tempering temperatures and times were targeted to achieve three different martensite volume fractions as a function of nickel content, with a nominal content varying between 0, 1, and 3-wt% Ni. Mechanical properties were characterized using tensile testing and microhardness measurements. Additionally, the microstructure was studied using scanning electron microscopy coupled with electron backscatter diffraction analysis. Tensile strength increased with increasing martensite ratio and nickel content, with a further grain refinement effect found in the 3-wt% Ni steel. The optimal heat treatment parameters for oil and gas and hydrogen transport applications are discussed.
Keywords: dual-phase steel; intercritical annealing; mechanical properties; microstructure characterization.