Titanium (Ti) alloys used for narrow dental implants usually contain aluminum (Al) and vanadium (V) for improved resistance. However, those elements are linked to possible cytotoxic effects. Thus, this study evaluated the biomechanical behavior of narrow dental implants made with Al- and V-free Ti alloys by the finite element method. A virtual model of a partially edentulous maxilla received single implants (diameter: 2.7 and 2.9 mm; length: 10 mm) at the upper lateral incisor area, with respective abutments and porcelain-fused-to-metal crowns. Simulations were performed for each implant diameter and the following eight alloys (and elastic moduli): (1) Ti-6Al-4V (control; 110 GPa), (2) Ti-35Nb-5Sn-6Mo-3Zr (85 GPa), (3) Ti-13Nb-13Zr (77 GPa), (4) Ti-15Zr (113 GPa), (5) Ti-8Fe-5Ta (120 GPa), (6) Ti-26.88Fe-4Ta (175 GPa), (7) TNTZ-2Fe-0.4O (107 GPa), and (8) TNTZ-2Fe-0.7O (109 GPa). The implants received a labially directed total static load of 100 N at a 45° angle relative to their long axis. Parameters for analysis included the maximum and minimum principal stresses for bone, and von Mises equivalent stress for implants and abutments. Ti-26.88Fe-4Ta reaches the lowest maximum (57 MPa) and minimum (125 MPa) principal stress values, whereas Ti-35Nb-5Sn-6Mo-3Zr (183 MPa) and Ti-13Nb-13Zr (191 MPa) models result in the highest principal stresses (the 2.7 mm model surpasses the threshold for bone overload). Implant diameters affect von Mises stresses more than the constituent alloys. It can be concluded that the narrow implants made of the Ti-26.88Fe-4Ta alloy have the most favorable biomechanical behavior, mostly by mitigating stress on peri-implant bone.
Keywords: biomechanics; bone–implant interface; dental alloys; single tooth dental implant.